Thermal damage of conventional hard chromium coatings on 416 stainless steel

Keyphrases

• Air Cooling 50%
• Air-to-ground 50%
• As-deposited 50%
• Chromium 50%
• Chromium Coating 50%
• Coefficient of Thermal Expansion 50%
• Cone Surface 50%
• Cooling Rate 50%
• Electroplating 50%
• Hard Chromium Coating 100%
• Heating Effect 50%
• Heating Temperature 50%
• Heating-cooling 50%
• Increased Temperature 50%
• Indentation 50%
• Induced Cracking 100%
• Mechanical Damage 50%
• Optical Microscope 50%
• Residual Stress 50%
• Residual Stress State 50%
• Resistance to Corrosion 50%
• Resistance to Wear 50%
• Spherical Indentation 50%
• Stainless Steel 100%
• Temperature Rate 50%
• Thermal Damage 100%
• Thermally Induced 100%
• Water Quenching 50%

Engineering

• Cooling Air 50%
• Cooling Rate 50%
• Expansion Coefficient 50%
• Hard Chromium 100%
• Heating Temperature 50%
• Increasing Temperature 50%
• Indentation 100%
• Mechanical Damage 50%
• Optical Microscope 50%
• Residual Stress 100%
• Stainless Steel 100%
• Stress State 50%